AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar

AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar

Categories:Steel tubes

Model No.:AISI 4330V

OD: 8-500mm

WT:10-250mm

Length: as your request.

DETAIL INFORMATION

AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar


Specification

Product NameForged QT Boring Alloy Steel Bar For Oil Services
SpecificationAPI 5CT/5CP/6A
Steel Grade4130, 4140, 4145, 4145H, 4330V, 4137, 4340
ProcessHot Forged+QT+Boring
Forged Bar Diameter8-500mm
Boring Hole Diameter10-250mm
LengthMax14 meters
InspectionSize, Chemical, Mechanical, UT, Drift Test, Low/High Temp. Impact
CertificateMTC, CO/FE/FA, BV/SGS
MOQ1-5 tons
Delivery Time10-30 days
Trade ItemFOB CIF CFR PPU PPD
PackagingLoose/Bundle/Wooden Pallet/Wooden Box/Plastic Cloth Wraps /Plastic End Caps/Beveled Protector

Introduce

AISI 4330V MOD is a modification of the 4330 alloy steel grade, with hardenability and other characteristics improved by the addition of vanadium. Alloy Steel 4330V offers good formability which is used for those that require a good combination of strength and impact resistance.

Applications

Shock loading or stress concentration applications are suited to this steel specification. 4330V is widely used in the oil and gas industry for applications such as oil tools, drill jars and shoes, tool holders and reamers and in the aerospace industry for applications such as bolting and air frames.

Standards

AMS 6427, AMS 6359, AMS 6304, ASTM A646, API 7 Specification

Chemicals Composition

GradeCMn maxSi maxCrMoNiP maxS maxV
4330V0.2-0.301.00.800.40-0.600.30-0.501-1.50.0250.0100.05-0.10

Mechanical Properties

Yield strength Rp0.2,

MPa

Tensile strength Rm,

MPa

Elongation

[%]
Hardness

[HBW]
Impact, Charpy-V, -20ºC

[J]
 1034 1138 15 341-388 32

Heat Treatment

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.

Annealing

Heat the steel slowly to 820-860°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 580°C followed by air cooling.

Stress Relieving

When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.

Hardening

4330V steel is usually supplied ready heat treated to 35-39 HRc. If further heat treatment is required annealed 4330V should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.

Tempering

Heat carefully to a suitable temperature selected by reference to a tempering chart or table, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air.

Forging

Preheat the steel carefully, then raise the temperature to 1070-1230°C for forging. Do not forge below 850°C. 4330V has good forging characteristics but care must be taken when cooling the steel due to its susceptibility to cracking. Cooling in ash or lime after forging is recommended.

Machining

Normalize and Temper at 1250°F(677°C) maximum prior to rough machine. This steel may also be machined at maximum strength, but machining must then be followed with a stress relieving at approximately 400°F(204°C).

Weldability

The steel has good welding characteristics and can be welded by resistance flash welding.

Mill′s test certificate

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing


Products Related

Enquiry

Company*

Name*

Phone

Email*

Want to know more?

If you want to know more or have any questions about our products, please feel free to contact us by phone or email.


Tel:86-21-35316960
Email:admin@shunitesteel.com